Teroson WT S3000 BK black coating against chipping and stone chipping on the chassis 1 L

TEROSON WT S3000 AQUA is based on a water coating with the addition of synthetic resins.
It can be applied with UBC guns, spatulas or paint splashes. The drying time depends on the thickness of the applied coating and the ambient temperature and relative humidity.
With good ventilation, drying is much faster + at a relatively high temperature. Dry matter adheres well to galvanized and galvanized steel sheet, metal and painted surfaces.

Advantages

Thanks to its high abrasion resistance and high flexibility, Teroson WT3000 AQUA provides excellent protection against scratches and stone chips. The resistance and good flexibility of TEROSON WT S3000 AQUA provides excellent protection against scratches and stone chips. TEROSON WT S3000 AQUA can be painted with waterborne paints. After complete drying (min. 6 hours), the coating can be painted with standard varnishes. After complete drying, the coating can be sanded.

TEROSON WT S3000 AQUA can be diluted with deionized water. For TEROSON WT S3000 AQUA dyeing, it is recommended not to exceed 30 vol.% of ready-to-use water-based paint. By changing the mixing proportions, spray pressure and distance from different surfaces, you can get surfaces from smooth to rough.

Applying

TEROSON WT S3000 AQUA is applied with a Henkel pistol
UBC-Gun with 1-l-cans. Recommended working pressure
is 3 - 5 bar. Shake well before use.

Painting

TEROSON WT S3000 AQUA can be painted with water
paint as well as solvent-based paint. Due to the variety of paints
of those on the market should be carried out preliminary tests.
Waterborne paints
TEROSON WT S3000 AQUA can be varnished at the earliest 6 hours after application (matte surface), but not later than 72 hours after application.

Conventional paints (solvent-based)
TEROSON WT S3000 AQUA can be varnished after full drying up to 72 hours after application